Features of structural transformations in ferroelectric ceramics PbZr1-xTixO3 (PZT) with x ≤ 0,08.

A.A. Spivakov1, Y.N. Zakharov1, E.M. Panchenko1, A.G. Lutochin1
1Institute of Physics SFU, 344090, pr. Stachki, 194
Abstract
Dielectric and pyroelectric properties of ceramics PbZr1-xTixO3 (PZT) in the concentration range 0.01<x<0.08 were investigate. As a matter of record it was found that in the PZT there is a region wherein appear three inhevent for the entire family of perovskite instabilities of original cubic lattice. It is shown that the antiferroelectric phase in PZT exists up to x=0.07. Studies of a composition with x = 0.08 in the temperature range -200ºC<T<300ºC had not revealed existence of antiferroelectric phase that makes evident the existence of vertical boundary between the Pbam and R3c phases.
Received: 18 October 2013   Revised: 06 November 2013   Accepted: 11 November 2013
Views: 79   Downloads: 14
References
1.
M. E. Lines and A. M. Glass. «Principles and Applicationsof Ferroelectrics and Related Materials» Clarendon,Oxford. (1977).
2.
D. E. Cox, B. Noheda, G. Shirane, Y. Uesu, K. Fujishiro, andY. Yamada, Appl. Phys. Lett. 79, 400 (2001).
3.
F. Cordero, F. Craciun, C. Galassi. Journal of Physics andChemistry of Solids, 69, 2172 (2008).
4.
W. Cochran, A. Zia. Phys. Stat. Sol., 25, 273 (1968).
5.
B. Jaffe, W. Cook, H. Jaffe. «Piezoelectric ceramics»,Academic Press, London and New York, 127 (1971).
6.
V.V. Eremkin, V.A. Smotrakov and E.G. Fesenko.Ferroelectrics. 110,137 (1990).
7.
R. Eitel, C. A. Randall. Phys. Rev. B, 75, 094106 (2007).
8.
F Cordero, F Trequattrini, F. Craciun and C. Galassi. J.Phys.: Condens. Matter, 23(41), 415901 (2011).