Generation of fragmented structures on the friction surface and wear particles of WC – (Fe-Mn-C) composites during high-speed sliding against the tool steel

И.Н. Севостьянова, Н.Л. Савченко, С.Н. Кульков show affiliations and emails
Accepted  24 April 2013
This paper is written in Russian
Citation: И.Н. Севостьянова, Н.Л. Савченко, С.Н. Кульков. Generation of fragmented structures on the friction surface and wear particles of WC – (Fe-Mn-C) composites during high-speed sliding against the tool steel. Lett. Mater., 2013, 3(2) 133-136
BibTex   https://doi.org/10.22226/2410-3535-2013-2-133-136

Abstract

Experimental studies of the subsurface layer structure and wear particles of WC – (Fe-Mn-C) MMC with structurally unstable binder phase after high-speed sliding over a steel disk have been carried out at the sliding speed 1 to 37 m/s under a normal stress 5 MPa.

References (5)

1. Гнюсов С.Ф., Савченко Н.Л., Севостьянова И.Н., Кульков С.Н. Формирование трибослоев на повер-хности композита WC - сталь Гадфильда после сухо-го трения по стали. Перспективные материалы, 2011, спец выпуск № 12, С. 449-454.
2. Колубаев А.В., Тарасов С.Ю., Сизова О.В., КолубаевЕ.А, Иванов Ю.Ф. Эволюция структуры поверхност-ного слоя металлов в условиях трения скольжения.Трение и износ, 2007, № 6, С. 582-590.
3. Кульков С.Н., Гнюсов С.Ф. Карбидостали на основекарбидов титана и вольфрама. Томск: Изд-во НТЛ, 2006, 240 с.
4. Севостьянова И.Н., Гнюсов С.Ф., Гармс А.П., КульковС.Н. Влияние термической обработки и соста-ва матрицы на формирование физико-механиче-ских свойств твердых сплавов WC- (Fe-Mn-C).Перспективные материалы. 1998, № 4, С. 37-41.
5. Севостьянова И.Н., Гнюсов С.Ф., Кульков C.Н.Деформация и разрушение карбидвольфрамовыхкомпозиционных материалов со структурно-неу-стойчивой матрицей. МиТОМ. 2009, № 6 (648), С.46-.

Similar papers