Abstract
Increased requirements for the strength properties of low-alloy steels stimulate the search for their new processing methods. Such improvements are accompanied by lowering impact toughness, especially at subzero temperatures. In this study, the possibilities of enhancing both tensile strength and low-temperature impact toughness of the Х70 grade steel by deformation thermocyclic treatment were investigated. Six cycles of heating the blanks, their helical rolling and cooling in water were carried out. In each cycle, the heating temperatures were gradually reduced from the initial level of 920°C down to the final value of 830°C. For comparison, two cooling media (water and air) were used after the final cycle. Then, the blanks were tempered at 550°C. After final cooling in air, the strength properties of the steel increased by about 15 % compared to that in the hot-rolled condition, while it enhanced by 2.5 times (σUTS up to 1200 MPa) after final cooling in water. For both media, it was not possible to improve the impact toughness. After final cooling in air, the reason was the formation of lath bainite areas, characterized by high microhardness values, in the soft ferrite matrix. In the second case, the martensitic microstructure with microhardness levels of up to 320 HV50 was observed. Additional tempering of the steel at 550°C significantly increased impact toughness at subzero temperatures (KCV−40°C = 220 – 260 J / cm2). Its combination with preliminary final cooling in water ensured both high strength properties (σUTS up to 900 MPa) and the absence of the ductile-to-brittle transition down to −70°C. The reason was the formed fine-grained microstructure, in which uniformly distributed phases possessed similar properties. The obtained results enabled to recommend the applied mode of deformation thermocyclic treatment for the Х70 grade steel that ensures the achievement of improved both strength properties and impact toughness.
References (23)
6. A. A. Shmatov, Thermocyclic treatment methods for volume strengthening steel tools, International Journal of Applied and Fundamental Research 7 (2021) 56 - 60. (in Russian) [A. А. Шматов, Методы термоциклической обработки для объемного упрочнения стальных инструментов, Международный Журнал Прикладных и Фундаментальных Исследований 7 (2021) 56 - 60.].
7. V. M. Konstantinov, D. M. Berdieva, A. A. Yusupov, G. A. Tkachenko, Investigation of the features of the structure formation of pre-eutectoid structural steels under various modes of thermocyclic treatment, Metallurgy: Republican Interdepartmental Collection of Scientific Papers 42 (2021) 258 - 269. (in Russian) [В. М. Константинов, Д. М. Бердиев, А. А. Юсупов, Г. А. Ткаченко, Исследование особенностей структурообразования доэвтектоидных конструкционных сталей при различных режимах термоциклической обработки, Металлургия: Республиканский Межведомственный Сборник Научных Трудов 42 (2021) 258 - 269.].
8. S. S. Yugai, M. G. Zakirova, T. R. Ablyaz, Dispersion of low-carbon martensitic steel by intensive thermocyclic treatment, Proceedings of the Samara Scientific Center of the Russian Academy of Sciences, 14 (2012) 1347 -1350. (in Russian) [С. С. Югай, М. Г. Закирова, Т. Р. Абляз, Диспергирование низкоуглеродистой мартенситной стали методом интенсивной термоциклической обработки, Известия Самарского Научного Центра Российской Академии Наук 14 (2012) 1347 - 1350.].
9.
V. E. Gordienko, A. A. Abrosimova, O. V. Kuz’min, E. V. Trunova, A. P. Scherbakov, The influence of thermal and thermal-cycle processing on the mechanical properties of structural steel, Bulletin of Civil Engineers 1 (2018) 128 -133. (in Russian) [В. Е. Гордиенко, А. А. Абросимова, О. В. Кузьмин, Е. В. Трунова, А. П. Щербаков, Влияние термической и термоциклической обработки на механические свойства конструкционных сталей, Вестник гражданских инженеров 1 (2018) 128 -133.]10. A. Prudnikov, M. Popova, V. Prudnikov, Hardening low carbon steel 10 by using of thermal-cyclic deformation and subsequent heat treatment, Materials Science. Non-Equilibrium Phase Transformations 2 (2016) 10 -13.
12.
V. V. Natarajan, S. Liu, V. S. A. Challa, R. D. K. Misra, D. M. Sidorenko, M. D. Mulholland, M. Manohar, J. E. Hartmann, Processing-structure-mechanical property relationship in Ti-Nb microalloyed steel: Continuous cooling versus interrupted cooling, Mater. Sci. Eng., A 671 (2016) 254 - 26320. S. Yu. Nastich. Ferritic − Bainitic Structure and Ductile Fracture Resistance of High Strength Pipe Steels, Russian Metallurgy (Metally) 10 (2013) 765-771.
Funding
1. Ministry of Science and Higher Education of the Russian Federation - FWRW-2021-0009