Physico-chemical properties of silicon-carbon films obtained by electrochemical deposition

I.Y. Bogush, N.K. Plugotarenko ORCID logo , T.N. Myasoedova, V.V. Ptashnik показать трудоустройства и электронную почту
Получена 05 сентября 2022; Принята 18 ноября 2022;
Эта работа написана на английском языке
Цитирование: I.Y. Bogush, N.K. Plugotarenko, T.N. Myasoedova, V.V. Ptashnik. Physico-chemical properties of silicon-carbon films obtained by electrochemical deposition. Письма о материалах. 2023. Т.13. №1. С.39-44
BibTex   https://doi.org/10.22226/2410-3535-2023-1-39-44

Аннотация

Physico-chemical properties of silicon-carbon films obtained by electrochemical depositionPure silicon-carbon films and the films doped with manganese or nickel were deposited on a copper foil by the electrochemical method from a methanol / hexamethyldisilazane solution. Scanning electron microscopy studies of silicon-carbon films showed a complex structure due to the presence of three-dimensional agglomerates and “leafy” structures. Raman spectroscopy showed that the silicon-carbon films were highly defective. The porosity study revealed that all samples mostly contained mesopores with sizes of 10 – 50 nm. The nickel-containing samples showed a more stable bimodal distribution of the mesopores. The highest specific surface area was observed for the manganese-containing silicon carbon films.

Ссылки (35)

1. T. Lin, I. W. Chen, F. Liu, C. Yang, H. Bi, F. Xu, F. Huang. Science. 350, 1508 (2015). Crossref
2. V. Subramanian, C. Luo, A. M. Stephan, K. Nahm, S. Thomas, B. Wei. J. Phys. Chem. C. 111, 7527 (2007). Crossref
3. M. Yu, Y. Han, Y. Li, J. Li, L. Wang. Carbohyd. Polym. 199, 555 (2018). Crossref
4. L. L. Zhang, X. Zhao. Chem. Soc. Rev. 38, 2520 (2009). Crossref
5. T. Kim, G. Jung, S. Yoo, K. S. Suh, R. S. Ruoff. ACS Nano. 7, 6899 (2013). Crossref
6. Q. Cao, Y. Zhang, J. Chen, M. Zhu, C. Yang, H. Guo, Y. Song, Y. Li, J. Zhou. Ind. Crops Prod. 148, 112181 (2020). Crossref
7. X. Li, W. Zhang, M. Wu, S. Li, X. Li, Z. Li. Int. J. Biol. Macromol. 183, 950 (2021). Crossref
8. J. Xia, N. Zhang, S. Chong, Y. Chen, C. Sun. Green Chemistry. 20, 694 (2018). Crossref
9. C. C. Viggi, S. Simonetti, E. Palma, P. Pagliaccia, C. Braguglia, S. Fazi, S. Baronti, M. A. Navarra, I. Pettiti, C. Koch et al. Biotechnol. Biofuels. 10, 303 (2017). Crossref
10. A. Berrueta, A. Ursua, I. San Martin, A. Eftekhari, P. Sanchis. IEEE Access. 7, 50869 (2019). Crossref
11. C. B. Amara, H. Hammami, S. Fakhfakh, et al. J. Electron. Mater. 50, 5915 (2021). Crossref
12. C. Wu, Y. Zhu, M. Ding, C. Jia, K. Zhang. Electrochim. Acta. 291, 249 (2018). Crossref
13. Q. X. Xia, K. S. Hui, K. N. Hui, S. D. Kim, J. H. Lim, Y. C. Si, et al. J. Mater. Chem. 2, 22102 (2015). Crossref
14. G. Gao, H. B. Wu, S. Ding, L. M. Liu, X. W. Lou. Small. 11 (7), 804 (2014). Crossref
15. L. Deng, H. Qu, Y. Zhang, S. Jiao, X. Zhang, K. Liu, et al. J. Solid State Chem. 281, 121026 (2018). Crossref
16. M. Feng, J. Gu, G. C. Zhang, M. Xu, Y. Yu, X. Liu, et al. J. Solid State Chem. 282, 121084 (2020). Crossref
17. F. Naseri, S. Karimi, E. Farjah, E. Schaltz. Renew. Sust. Energ. Rev. 155, 111913 (2022). Crossref
18. X. B. Yan, B. K. Tay, G. Chen, S. R. Yang. Electrochem. Commun. 8 (5), 737 (2006). Crossref
19. H. Zhuang, N. Yang, L. Zhang, R. Fuchs, X. Jiang. Appl. Mater. Int. 7 (20), 10886 (2015). Crossref
20. C.-H. Chang, B. Hsia, J. P. Alper, S. Wang, L. E. Luna, C. Carraro, S.-Y. Lu, R. Maboudian. ACS Appl. Mater. Int. 7(48), 26658 (2015). Crossref
21. T. Nakayamada, K. Matsuo, Y. Hayashi, A. Izumi, Y. Kadotani. Thin solid films. 516, 656 (2008). Crossref
22. S. Manocha, D. Ankur, L. M. Manocha. Eurasian Chem Tech Journal. 13, 27 (2011). Crossref
23. J. J. Senkevich, et al. Applied Physics A: Mat. Sc. 77 (3), 581 (2003). Crossref
24. M. N. Grigoryev, T. N. Myasoedova, T. S. Mikhailova. J. Phys.: Conf. Ser. 1124, 081043 (2018).
25. N. K. Plugotarenko, T. N. Myasoedova, I. Y. Bogush. Materials Science in Semiconductor Processing. 135, 106121 (2021). Crossref
26. T. N. Myasoedova, M. N. Grigoryev, T. S. Mikhailova. Journal of Alloys and Compounds. 855 (2), 157504 (2021). Crossref
27. M. S. Javed, S. S. A. Shah, S. Hussain. Chemical Engineering Journal. 382, 122814 (2020). Crossref
28. J. Jagiello, A. Chojnacka, S. E. M. Pourhosseini, Z. Wang, F. Beguin. Carbon. 178, 113 (2021). Crossref
29. A. Kaniyoor, S. Ramaprabhu. Aip Adv. 2, 032183 (2012). Crossref
30. V. Georgakilas, J. A. Perman, J. Tucek, R. Zboril. Broad Chemical Reviews. 115, 4744 (2015). Crossref
31. K. N. Kudin, et al. Nano Letters. 8, 36 (2008). Crossref
32. A. C. Ferrari, D. M. Basko. Nat Nano. 8, 235 (2015). Crossref
33. M. Iijima, H. Kamiya. J. Phys. Chem. C. 112, 11786 (2008). Crossref
34. M. Yu, W. Wang, C. Li, et al. Asia Mater. 6, e129 (2014). Crossref
35. S. Lafon-Placette, K. Delbé, J. Denape, M. Ferrato. Journal of the European Ceramic Society. 35 (4), 1147 (2014). Crossref

Финансирование на английском языке

1. Southern Federal University - Strategic Academic Leadership Program of the Southern Federal University ("Priority 2030")