Annealing-induced recrystallization of iron after high pressure torsion at 80 K

K.E. Shugaev, M.V. Degtyarev, L.M. Voronova ORCID logo , T.I. Chashchukhina ORCID logo , T.M. Gapontseva показать трудоустройства и электронную почту
Получена 11 января 2022; Принята 15 марта 2022;
Эта работа написана на английском языке
Цитирование: K.E. Shugaev, M.V. Degtyarev, L.M. Voronova, T.I. Chashchukhina, T.M. Gapontseva. Annealing-induced recrystallization of iron after high pressure torsion at 80 K. Письма о материалах. 2022. Т.12. №2. С.94-99
BibTex   https://doi.org/10.22226/2410-3535-2022-2-94-99

Аннотация

Grain growth during recrystallization of pure iron with a submicrocrystalline structure formed by high-pressure torsion deformation at cryogenic temperatureGrain growth during recrystallization of pure iron with a submicrocrystalline structure formed by 5 revolutions of an anvil of high-pressure torsion deformation at cryogenic temperature (80 К) has been studied by transmission and scanning electron microscopy and durometry. Annealing at 523 К has significantly developed recrystallization (to 90 % of the material volume). The average recrystallized grain size is 2 μm. The primary recrystallization has been completed after 1‑h annealing at 823 К, forming grains with an average grain size of 6.5 μm. Annealing at 823 К has resulted in a large number of fine grains due to the formation of thermally activated centers of recrystallization. The grain size variability, which is characterized by the formation of grains with a size of five or more times greater than the average grain size, is observed. The average grain size has remained unchanged according to the scanning electron microscopy data, and decreased according to transmission electron microscopy data. The recrystallization texture of an axial <110> type has formed during annealing at 823 К. An increase in the annealing temperature to 923 К has increased the sharpness of the recrystallization texture. The hardness of iron has remained dependent on the true strain (distance from the sample center) after annealing at all temperatures under study.

Ссылки (36)

1. K. Edalati, J. M. Cubero-Sesin, A. Alhamidi, I. F. Mohamed, Z. Horita. Mater. Sci. Eng. A. 613, 103 (2014). Crossref
2. A. V. Podolskiy, C. Mangler, E. Schafler, E. D. Tabachnikova, M. J. Zehetbauer. J. Mater. Sci. 48, 4689 (2013). Crossref
3. V. V. Popov, E. N. Popova, V. P. Pilyugin, D. D. Kuznetsov, A. V. Stolbovsky. IOP Conf. Series Mater. Sci. and Eng. 63, 012096 (2014). Crossref
4. V. V. Popov, E. N. Popova. Materials Transactions. 60, 1209 (2019). Crossref
5. V. V. Popov, E. N. Popova, D. D. Kuznetsov, A. V. Stolbovskii, V. P. Pilyugin. Phys. of Metals and Metallogr. 115, 682 (2014). Crossref
6. S. S. Gorelik. Recrystallization of Metals and Alloys. Moscow, MISIS (2005) 430 p. (in Russian) [С. С. Горелик, С. В. Добаткин, Л. М. Капуткина. Рекристаллизация металлов и сплавов. Москва, МИСИС (2005) 430 с.].
7. T. Sakai, A. Belyakov, R. Kaibyshev, H. Miura, J. J. Jonas. Progress in Materials Science. 60, 130 (2014). Crossref
8. X. Wang, P. Li, K. Xue. Procedia Manufacturing 15, 1487 (2018). Crossref
9. N. A. Smirnova, V. I. Levit, V. P. Pilyugin, R. I. Kuznetsov, M. V. Degtyarev. Phys. Met. Metallogr. 62 (3), 140 (1986).
10. M. V. Degtyarev, L. M. Voronova, V. V. Gubernatorov, T. I. Chashchukhina. Doklady Physics, 47 (9), 647 (2002). Crossref
11. L. M. Voronova, M. V. Degtyarev, T. I. Chashchukhina. Phys. Metals Metallogr. 104 (3), 262 (2007). Crossref
12. Yu. V. Ivanisenko, A. A. Sirenko, A. V. Korznikov. Phys. Metals Metallogr. 87, 329 (1999).
13. A. A. Popov, I. Yu. Pyshmintsev, S. L. Demakov, A. G. Illarionov, R. Z. Valiev. Phys. Metals Metallogr. 83, 550 (1997).
14. A. P. Zhilyaev, T. G. Langdon. Progress in Materials Science. 53, 893 (2008). Crossref
15. J. Gubicza, N. Q. Chinh, E. Khosravi, S. V. Dobatkin, T. G. Langdon. Key Engineering Materials. 465, 195 (2011). Crossref
16. L. M. Voronova, T. I. Chashchukhina, M. V. Degtyarev. Phys. Metals Metallogr. 119, 969 (2018). Crossref
17. N. A. Smirnova, V. I. Levit, M. V. Degtyarev. Phys. Metals Metallogr. 66 (5), 185 (1988).
18. V. P. Pilyugin, L. M. Voronova, M. V. Degtyarev, T. I. Chashchukhina, V. B. Vykhodets, T. E. Kurennykh. Phys. Metals Metallogr. 110, 564 (2010). Crossref
19. M. V. Degtyarev, L. M. Voronova, T. I. Chashchukhina. Russian Metallurgy (Metally). 2005 (5), 390 (2005).
20. L. M. Voronova, M. V. Degtyarev, T. I. Chashchukhina. Phys. Metals Metallogr. 109, 135 (2010). Crossref
21. H. W. Zhang, X. Huang, R. Pippan, N. Hansen. Acta Materialia. 58, 1698 (2010). Crossref
22. H. H. Bernardi, H. R. Z. Sandim, K. D. Zilnyk, B. Verlinden, D. Raabe. Materials Research. 20 (5), 1238 (2017). Crossref
23. F. J. Humphreys. J. Mater. Sci. 36 (16), 3833 (2001). Crossref
24. S. A. Saltykov. Stereometric Metallography. Moscow, Metallurgiya (1976) 270 p. (in Russian) [С. А. Салтыков. Стереометрическая металлография. Москва, Металлургия (1976) 270 с.].
25. J.-l. Ning, E. Courtois-Manara, L. Kurmanaeva, A. V. Ganeev, R. Z. Valiev, Ch. Kübel, Yu. Ivanisenko. Mater. Sci. and Eng. A. 581, 8 (2013). Crossref
26. D. P. Field, L. T. Bradford, M. M. Nowell, T. M. Lillo. Acta Mater. 55, 4233 (2007). Crossref
27. A. Yu. Eroshenko, Yu. P. Sharkeev, M. A. Khimich, I. A. Glukhov, P. V. Uvarkin, A. I. Tolmachev, A. M. Mairambekova. Lett. on Mater. 10 (1), 54 (2020). (in Russian) [А. Ю. Ерошенко, Ю. П. Шаркеев, М. А. Химич, И. А. Глухов, П. В. Уваркин, А. И. Толмачев, А. М. Майрамбекова. Письма о материалах. 10 (1), 54 (2020).]. Crossref
28. V. N. Perevezentsev, A. S. Pupynin, A. E. Ogorodnikov. Lett. on Mater. 9 (1), 107 (2019). Crossref
29. L. M. Voronova, M. V. Degtyarev, T. I. Chashchukhina. Phys. Metals Metallogr. 122, 559 (2021). Crossref
30. M. Degtyarev, T. Chashchukhina, L. Voronova, T. Gapontseva, V. Levit. International Journal of Refractory Metals & Hard Materials. 86, 105117 (2020). Crossref
31. V. Yu. Novikov. Secondary recrystallization. Moscow, Metallurgy (1990) 128 p. (in Russian) [В. Ю. Новиков. Вторичная рекристаллизация. Москва. Металлургия (1990) 128 с.].
32. C. Moussa, M. Bernacki, R. Besnard, N. Bozzolo. IOP Conf. Series: Mater. Sci. and Eng. 89, 012038 (2015). Crossref
33. M. Calcagnotto, D. Ponge, E. Demir, D. Raabe. Mater. Sci. and Eng. A. 527, 2738 (2010). Crossref
34. L. M. Voronova, M. V. Degtyarev, T. I. Chashchukhina, D. V. Shinyavskii, T. M. Gapontseva. Lett. on Mater. 7 (4), 359 (2017). Crossref
35. J. Duana, H. Wen, C. Zhou, R. Islamgaliev, X. Li. Materialia. 6, 100349 (2019). Crossref
36. J. Duan, H. Wen, C. Zhou, X. He, R. Islamgaliev, R. Valiev. J. Mater. Sci. 55, 7958 (2020). Crossref

Другие статьи на эту тему

Финансирование на английском языке

1. the state assignment themes “Pressure” - 122021000032-5